WearPro Pipes

pipes

Reasons to Consider Using WearPro Pipes:

  • Anti-Scaling
  • Superior Chemical Resistivity (for details click here)
  • Superior Abrasion and Impact resistance to EnergyPro
    (click here for testing report)
  • Extreme Wear Resistance
  • Extremely Low Surface Roughness
  • Self Lubricating
  • Improves Pumping Efficiency
  • Reduces Required Energy Input
  • Greatly Reduces 'Total Pumping Cost'
  • Corrosion Resistance
  • Aids in Delivering Emmision Targets

pipe Try our friction loss calculator to see how much you can save by using our products

Suitable Applications for WearPro Pipes are:

  • Dredging
  • Mineral sand
  • Mine tailings line
  • Water pipelines
  • Waste Water and sewerage pipelines

Pipe & Buoy Australia is the only UHMWPE pipe manufacturer in the world. We are not just a "materials" company:

Custom sizes available, where moulds already exist from 20-1400mm OD, up to 65 WT. Product can be manufactured in any colour, and to all conformance requirements.

  • The only extruder to enforce ISO 9001, 14001, and OHSAS 18001 certifications exclusively
  • The only extruder capable of pipe >45mm WT and >800mm OD (Capable of 65mm and 1400 OD respectively)
  • Our PipePro range is such, that we are the only pipe company that will refuse to sell HDPE pipe for slurry applications

Case Studies

Pressure Rating

Stocklist

PropertyRaw Material Values Only
PHYSICAL PROPERTIES
Raw MaterialWearPro
Density (kg/m3)≥ 930
Water Absorption 24hrs(%) <0.01
MECHANICAL PROPERTIES
Tensile strength at Break (Mpa)≥ 29
Elongation at Break(%)≥ 300
Impact strength(KJ/㎡)≥ 70
Wear Loss (Factory test) < 28%
Coefficient of Friction (unplaned)0.12
Shore Hardness( R)61- 68
THERMAL PROPERTIES
Coefficient of Linear Expansion(10-4)1.5
Heat Deflection Temp at 0.45 Mpa(℃)≥ 50
ELECTRICAL PROPERTIES
Surface Resistivity(Ohm)1109Ω
CHEMICAL PROPERTIES
Hydrochloric AcidNo abnormal in the sample surface immersed in 20℃-80℃ of hydrochloric acid
Phosphoric AcidNo abnormal in the sample surface immersed in 20℃-80℃ of phosphoric
93# gasolineNo abnormal in the sample surface immersed in 20℃-80℃ of 93#
Acetic acidNo abnormal in the sample surface immersed in 20℃-80℃ of glacial acetic acid
Sodium hydroxideNo abnormal in the sample surface immersed in 20℃-80℃ of sodium hydrox-
502 super glueNo bonding between samples surfaces