EnergyPro Pipes

pipes

Reasons to Consider Using EnergyPro Pipes:

pipe Try our friction loss calculator to see how much you can save by using our products

Suitable Applications for EnergyPro Pipes are:

  • Chutes
  • Launders
  • High scaling Zones
  • Low wear rate dredging
  • Low wear rate tailing
  • Chemical transfer
  • Fly ash
  • Hypersaline brine
  • Hyprotransport
  • Conveyors
  • Spiral distributors
  • Concentrate
  • Sour gas transport
  • Mineral processing
  • Overflow and underflow areas of low wear
  • Pipe & Buoy Australia is the only UHMWPE pipe manufacturer in the world. We are not just a "materials" company:

    Custom sizes available, where moulds already exist from 20-1400mm OD, up to 65 WT. Product can be manufactured in any colour, and to all conformance requirements.

    • The only extruder to enforce ISO 9001, 14001, and OHSAS 18001 certifications exclusively
    • The only extruder capable of pipe >45mm WT and >800mm OD (Capable of 65mm and 1400 OD respectively)
    • Our PipePro range is such, that we are the only pipe company that will refuse to sell HDPE pipe for slurry applications

    Case Studies

    Stocklist

    PropertyRaw Material Values Only
    PHYSICAL PROPERTIES
    Raw MaterialEnergyPro
    Density (kg/m3)≥ 930
    Water Absorption 24hrs(%) <0.01
    MECHANICAL PROPERTIES
    Tensile strength at Break (Mpa)≥ 29
    Elongation at Break(%)≥ 300
    Impact strength(KJ/㎡)≥ 80
    Wear Loss (Factory test) < 30%
    Coefficient of Friction (unplaned)0.12
    Shore Hardness( R)61- 68
    THERMAL PROPERTIES
    Coefficient of Linear Expansion(10-4)1.5
    Heat Deflection Temp at 0.45 Mpa(℃)≥ 50
    ELECTRICAL PROPERTIES
    Surface Resistivity(Ohm)1109Ω
    CHEMICAL PROPERTIES
    Hydrochloric AcidNo abnormal in the sample surface immersed in 20℃-80℃ of hydrochloric acid
    Phosphoric AcidNo abnormal in the sample surface immersed in 20℃-80℃ of phosphoric
    93# gasolineNo abnormal in the sample surface immersed in 20℃-80℃ of 93#
    Acetic acidNo abnormal in the sample surface immersed in 20℃-80℃ of glacial acetic acid
    Sodium hydroxideNo abnormal in the sample surface immersed in 20℃-80℃ of sodium hydrox-
    502 super glueNo bonding between samples surfaces